PRODUCT CATEGORIES
-
ALUMINIUM
- ATOMIZED ALUMINIUM POWDER
- SPHERICAL ALUMINIUM POWDER
- ALUMINIUM ALLOY POWDER
- FERRO ALUMINIUM POWDER
- LEAFING ALUMINIUM PASTE - STANDARD ..
- WATERBORNE ALUMINIUM PASTE - SPECIA..
- NON LEAFING ALUMINIUM PASTE - STAND..
- LEAFING ALUMINIUM POWDER – STANDA..
- NON LEAFING ALUMINIUM POWDER- SPECI..
- COLORED ALUMINIUM POWDER - SPECIALI..
- ALUMINIUM PELLETS & GRANULES- SPECI..
- ALUMINIUM POWDERS FOR FIREWORKS, SL..
- ALUMINIUM POWDER FOR PESTICIDES
- ALUMINIUM POWDER FOR LIGHT WEIGHT C..
- ALUMINIUM PASTE FOR LIGHT WEIGHT CO..
- BISMUTH
- COPPER
- CALCIUM SILICIDE
- COBALT
- GOLD BRONZE
- MAGNESIUM
- PHOSPHORUS
- SILICON
- SILVER
- TIN
- TITANIUM
- TUNGSTEN
- ZINC
ALUMINIUM PASTE FOR LIGHT WEIGHT CONCRETE–(80/20) & (70/30)
Aluminium Pastes for Light weight concrete: (80/20)
| Parameters |
Non Volatile Matter (%) |
Particle Size-Wet Sieve <45 µm (%) |
*Particle Size Distribution D (50%) (µm) |
*Active Al content (%) |
Solvent | Application |
Recommended AAC block density (kg/m3) |
|
|
(ISO-1247) | (ISO-1247) | (Malvern-2000) | (IS-438) | |||
| CO 66D (80/20) | 80±3 | 53 - 72 | 50 - 60 | 91 min | DEG |
 |
600 - 700 |
| CO 77D (80/20) | 80±3 | 70 - 81 | 40 - 50 | 90 min | DEG |
|
500 - 600 |
| CO 88D (80/20) | 80±3 | 83 - 94 | 25 - 35 | 90 min | DEG |
|
400 - 500 |
| CO 88DP (80/20) | 80±3 | 83 - 94 | 25 - 35 | 90 min | DEG |
|
400 - 500 |
| CO 88G (80/20) | 80±3 | 83 - 94 | 25 - 35 | 90 min | HG |
|
400 - 500 |
| CO 88GP (80/20) | 80±3 | 83 - 94 | 25 - 35 | 90 min | HG |
|
400 - 500 |
| CO 99D (80/20) | 80±3 | 90 min | 20 - 30 | 90 min | DEG |
|
350 - 400 |
| CO 99DP (80/20) | 80±3 | 90 min | 20 - 30 | 90 min | DEG |
|
350 - 400 |
| CO 99G (80/20) | 80±3 | 90 min | 20 - 30 | 90 min | HG |
|
350 - 400 |
| CO 99GP (80/20) | 80±3 | 90 min | 20 - 30 | 90 min | HG |
|
350 - 400 |
| NICO 99D (80/20) | 80±3 | 91.5 min | 15 - 20 | 90 min | DEG |
|
350 |
| NICO 99DP (80/20) | 80±3 | 91.5 min | 15 - 20 | 90 min | DEG |
|
350 |
The above grades are hydrophillic in nature and their gas evolution at 25ºC for 0.07 g of Al paste in 400 ml of 2 % CaO solution.: 60 ml min @ 16th minute.
Wet sieving with acetone as rinsing liquid
*Active Aluminium & PSD-before conversion.
Flake
DEG: Diethylene glycol
HG: Hexylene Glycol
(Used for Aerated light weight concrete plasters applications)
Aluminium Pastes for Light weight concrete : (70/30)
| Parameters |
Non Volatile Matter (%) |
Particle Size-Wet Sieve <45 µm (%) |
*Particle Size Distribution D (50%) (µm) |
*Active Al content (%) |
Solvent | Application |
Recommended AAC block density (kg/m3) |
|
|
(ISO-1247) | (ISO-1247) | (Malvern-2000) | (IS-438) | |||
| CO 66D (70/30) | 70±3 | 59 - 75 | 50 - 60 | 91 min | DEG |
|
600 - 700 |
| CO 77D (70/30) | 70±3 | 74 - 84 | 40 - 50 | 90 min | DEG |
|
500 - 600 |
| CO 88D (70/30) | 70±3 | 85 - 95 | 25 - 35 | 90 min | DEG |
|
400 - 500 |
| CO 88DP (70/30) | 70±3 | 85 - 95 | 25 - 35 | 90 min | DEG |
|
400 - 500 |
| CO 88G (70/30) | 70±3 | 85 - 95 | 25 - 35 | 90 min | HG |
|
400 - 500 |
| CO 88GP (70/30) | 70±3 | 85 - 95 | 25 - 35 | 90 min | HG |
|
400 - 500 |
| CO 99D (70/30) | 70±3 | 91 min | 20 - 30 | 90 min | DEG |
|
350 - 400 |
| CO 99DP (70/30) | 70±3 | 91 min | 20 - 30 | 90 min | DEG |
|
350 - 400 |
| CO 99G (70/30) | 70±3 | 91 min | 20 - 30 | 90 min | HG |
|
350 - 400 |
| CO 99GP (70/30) | 70±3 | 91 min | 20 - 30 | 90 min | HG |
|
350 - 400 |
| NICO 99D (70/30) | 70±3 | 92.5 min | 15 - 20 | 90 min | DEG |
|
350 |
| NICO 99DP (70/30) | 70±3 | 92.5 min | 15 - 20 | 90 min | DEG |
|
350 |
The above grades are hydrophillic in nature and their gas evolution at 25ºC for 0.07 g of Al paste in 400 ml of 2 % CaO solution.: 50 ml min @ 16th minute.
Wet sieving with acetone as rinsing liquid
*Active Aluminium & PSD-before conversion.
Flake
DEG: Diethylene glycol
HG: Hexylene Glycol
(Used for Aerated light weight concrete plasters applications)